The transparent texture of glass has a special aesthetic feeling, while the transparent raw materials make it play a special role in brightening light and expanding space in home decoration. If used properly, glass materials will build a romantic and romantic atmosphere for home life.

Compared with painted glass which is better? Colored glazed glass and lacquer glass belong to glass, mainly in the manufacturing process is different. Below Haihua Xiaobian mainly from the process, manufacturing process, function and other aspects to give you a detailed introduction.

1. The manufacturing process of colored glazed glass and lacquered glass

1, colored glazed glass

Colored glazed glass is the inorganic glaze through screen printing, roller printing, digital glaze printing and other glaze process coated on the surface of the glass, through drying, heating furnace heating to glass glaze melting condition, and through tempering quenching and cooling manufacturing. Through heating sintering, can make the glaze layer and glass long combination into one, so that the colored glaze glass has good acid and alkali resistance and safety. Colored glazed glass as a kind of architectural glass materials, its great characteristic is that it has decoration function, so that the decoration surface shows rich colors and patterns, and gives dynamic beauty with the change of light.

2, paint glass

Lacquer glass is a kind of expressive decoration glass, which can be expressed by spraying, rolling coating, screen printing or spraying and other methods, also called back paint glass, flat paint glass and frosted paint glass, commonly used in the background wall and other places in the center of the home. Lacquer glass is painted on the back of the glass in the 30-45 degree oven for 8-12 hours, in many places where the manufacture of lacquer glass generally uses natural sun drying, but the natural sun drying paint adhesion is relatively small, simple fall off in the humid environment.

Two, the manufacturing process of colored glazed glass and lacquered glass

Colored glazed glass: colored glazed glass is sprayed/painted/printed with inorganic glaze, and then baked by 620-720 high temperature, and the glass body as one.

Lacquered glass: lacquered glass is sprayed/painted/printed with organic/inorganic pigments mixed with organic/inorganic polymers, and then baked at 100-150 degrees Celsius.

Three, the performance of colored glazed glass and painted glass

Glazed glass for high temperature molding, glazed glass surface has formed a chemical combination, with a knife to scrape off, very firm, almost no change; Paint glass for low temperature molding, paint and glass surface is a physical combination, the test is the bonding performance of the paint, with the continuation of time, may flake, discoloration.

As for the impact resistance of glass, safety performance, depends on toughened glass, has nothing to do with glaze, paint.

Lacquered glass: lacquered glass is sprayed/painted/printed with organic/inorganic pigments mixed with organic/inorganic polymers, and then baked at 100-150 degrees Celsius.

Four, the function of colored glazed glass and lacquered glass

Glazed glass for high temperature molding, glazed glass appearance has formed a chemical combination, with a knife can not be scraped off, very strong, there will be no change; Paint glass for low temperature molding, paint and glass surface is a physical combination, the test is the bonding function of the paint, with the continuous time, may flake, discoloration.

As for the impact resistance function and safety function of glass, it depends on toughened glass, and has nothing to do with colored glaze and paint.